... 可能還有可取的地方，那簡單的hotend 如果能順地印pla 應十分不錯。它比e3d .得多，可以大幅簡化effector 設計和重量。
...
ustkl 發表於 2016-8-9 13:09 
“Tiko requires zero maintenance aside from periodic replacement of the nozzle. A nozzle will be included with every roll of Tiko filament (or can be purchases seperately), so if you replace it after each 1kg of printed filament, you’ll be just fine.“
... there will be a build up of charred plastic on the inner walls of the melting zone and metering zone sections of the liquefier. This is inevitable as there is always a slow moving boundary layer of melted plastic, which is “cooked” over time (especially PLA, as it has poor thermal stability). ..., https://all3dp.com/tiko-faq-on-all3dp/
 胡說八道一堆, 然後極之隱晦地說了, PLA不成. 其實 PLA不成 也很好理解的. 就算真的是鈦合金, 導熱速度也不過只是 比不鏽鋼 慢2成至3成, 另加沒有內藏PTFE管, 這就即是大倒退至 淘寶機都不能印PLA時期的那一種噴頭設計 了. |